Grade X30cr13 - 420 Stainless Steel

X30Cr13 is a martensitic grade of 420 stainless. It is a general purpose, free machining version of 420 stainless steel. Magnetic, hardenable with rust resistant properties. X30Cr13 stainless is characterised by having a 0.26-0.35 carbon, and 12-14% chromium content. This mix of analysis gives X30Cr13 an outstanding corrosion resistance and exceptional wear properties after heat treatment. Superior to 410 and 416 types for most applications. X30Cr13 has good ductility in the annealed condition, but is capable of achieving 51HRC after treatment. Optimal corrosion resistance is realised when X30Cr13 is surface ground and polished after hardening.

 X30Cr13 - 420 Stainless Steel  Chemical Analysis wt % 
C Si Mn P S Cr Ni
0.26-0.35 ≤ 1.50 ≤ 1.00 ≤ 0.04 ≤ 0.03 12.0-14.0 ≤ 1.00

Applications for X30Cr13

Dental and surgical instruments cutlery pump shafts gear pinions, cams and various hand tools

Not recommended for high pressure vessels.

Soft Annealing X30Cr13

Heat to 745-820°C. Cool slowly in air. 

Structure is ferrite with spherical carbides.

Machineability of X30Cr13

Good machining characteristics due to the addition of Sulphur.

High speeds and feeds producing short brittle chips

 X30Cr13 - 420 Stainless Steel Mechanical Properties at ambient temperature 

 Condition annealed. Quenched and tempered 850°C

 0.2% Proof Stress: 650 Nmm2

 Tensile Strength: 850 - 1000 Nmm2

 Elongation: 10% 

 Hardness HB Max 230

Forging X30Cr13

Hot forming temperature 800-1000°C. Slow cool

Hardening X30Cr13

Harden from a temperature 950-1050°C

Follow by oil or air quenching.

Hardness after quenching 45-51 HRC

Tempering X30Cr13

Tempering temperature 625-724°C

Heat Treatment Advise of X30Cr13

Treatment temperatures, including the rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each X30Cr13 - 420 stainless steel component. other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance for the heat treatment of X30Cr13

Corrosion resistance X30Cr13

Hardened condition realises resistance to atmosphere, fresh, dilute acids and alkalise, fresh water and fruit and vegetable juices

 X30Cr13 - 420 Stainless Steel  Physical properties  

 Average values at ambient temperature

 Modulus of elasticity.  (10³ x N/mm²) : 215 205 (200°C) 190 (400°C)

 Density.  (g/cm³): 7.73

 Thermal conductivity.  (W/m.K): 30.0

 Electric resistivity.  (Ohm mm²/m): 0.65

 Specific heat capacity.  (J/g.K): 0.46

 Magnetisable. Yes

Welding of X30Cr13

Not commonly welded due to its air hardening characteristics. Welding may possibly be performed after preheating to 150-205°C with the post welding tempering at temperature for 2 hours. Recommendation of specialist advice to be sought

Cold working of X30Cr13

Material will withstand only minor cold work. Radical forming operations will result in cracking


The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustrations to enable the reader to make their own evaluations. They are not intended to either express or imply the suitability for these or any other purposes 